Ask question

Ask question

All categories

3 years ago

5

Some states authorize a to make healthcare decisions ------- for patients who can't make them because they're incapacitated. O a

) healthcare proxy b) living will O c) durable power of attorney O d) do-not-resuscitate order

1 answer:

coldgirl [10]3 years ago

6 0

Answer:

A)healthcare proxy

Explanation:

A)healthcare proxy

A)healthcare proxy

You might be interested in

Why are alcohols classified as organic compounds?

Maslowich

Rubbing Alcohols are chemical compounds because rubbing alcohol itself is a strecture made up of many different chemicals combinding in a compound that make, C3H8O

5 0

3 years ago

The rate of decomposition of acetaldehyde, CH_3 CHO(g), into CH_4(g) and CO(g) in the presence of I_2(g) at 800 K follows the ra

FrozenT [24]

Answer:

Explanation:

Catalyst is I2 . Because I2 is reacted with starting material in step 1 and generated in second step

Rate limiting step is step 1. Because in rate equation CH3CHO and I2 is mentioned. Hence the overall rate of reaction is depending CH3CHO and I2. Rate limiting step is step 1

5 0

3 years ago

PLEASE HELP! It'll mean the world to me

Vikki [24]

Answer:

24 a 2.85

Explanation:

HCl is a powerful acid so it completely ioniz in water

8 0

3 years ago

Calculate the unit cell edge length for an 78 wt% Ag- 22 wt% Pd alloy. All of the palladium is in solid solution, and the crysta

BaLLatris [955]

Answer:

The unit cell edge length for the alloy is 0.405 nm

Explanation:

Given;

concentration of Ag, $C_{Ag}$ = 78 wt%

concentration of Pd, $C_P_d$ = 22 wt%

density of Ag = 10.49 g/cm³

density of Pd = 12.02 g/cm³

atomic weight of Ag, $A_A_g$ = 107.87 g/mol

atomic weight of iron, $A_P_d$ = 106.4 g/mol

Step 1: determine the average density of the alloy

$\rho _{Avg.} = \frac{100}{\frac{C_A_g}{\rho _A_g} + \frac{C__{Pd}}{\rho _{Pd}} }$

$\rho _{Avg.} = \frac{100}{\frac{78}{10.49} + \frac{22}{12.02} } = 10.79 \ g/cm^3$

Step 2: determine the average atomic weight of the alloy

$A _{Avg.} = \frac{100}{\frac{C_v}{A _A_g} + \frac{C__{Pd}}{A _{Pd}} }$

$A _{Avg.} = \frac{100}{\frac{78}{107.87} + \frac{22}{106.4} } = 107.54 \ g/mole$

Step 3: determine unit cell volume

$V_c=\frac{nA_{avg.}}{\rho _{avg.} N_a}$

for a FCC crystal structure, there are 4 atoms per unit cell; n = 4

$V_c=\frac{4*107.54}{ 10.79*6.022*10^{23}} = 6.620*10^{-23} \ cm^3/cell$

Step 4: determine the unit cell edge length

Vc = a³

$a = V_c{^\frac{1}{3} }\\\\a = (6.620*10^{-23}}){^\frac{1}{3}}\\\\a = 4.05 *10^{-8} \ cm$ = 0.405 nm

Therefore, the unit cell edge length for the alloy is 0.405 nm

7 0

3 years ago

Pouring cold water in your hot coffee is<br> conduction<br> convection<br> radiation

Sladkaya [172]

Convection this is because convection is bull movement of molecules between fluids

6 0

3 years ago

Read 2 more answers