A displacement transducer has the following specifications: Linearity error ± 0.25% reading Drift ± 0.05%/○C reading Sensitivity

White raven [17]

Answer:

The Estimated uncertainty in a nominal displacement of 2 cm at the design stage is plus or minus 0.0124cm

Explanation:

uncertainty in a nominal displacement

= (u^2 + v^2)^(1/2)

assume from specifications that k = 5v/5cm

= 1v/cm

u^2 = (0.0025*2)^(2) + (0.005*10*2)^2 + (0.0025*2)^2

= 0.01225v

v = 2v * 0.001

= 0.002v

uncertainty in a nominal displacement

= (u^2 + v^2)^(1/2)

= ((0.01225)^2 + (0.002)^2)^(1/2)

= 0.0124 cm

Therefore, The Estimated uncertainty in a nominal displacement of 2 cm at the design stage is plus or minus 0.0124cm

8 0

3 years ago

Consider a very long, slender rod. One end of the rod is attached to a base surface maintained at Tb, while the surface of the r

9966 [12]

Answer:

(a) Calculate the rod base temperature (°C). = 299.86°C

(b) Determine the rod length (mm) for the case where the ratio of the heat transfer from a finite length fin to the heat transfer from a very long fin under the same conditions is 99 percent. = 0.4325m

Explanation:

see attached file below

3 0

3 years ago

Implement the following Matlab code:

vagabundo [1.1K]

28384 *x soít cos estematema

3 0

3 years ago

The fracture strength of glass may be increased by etching away a thin surface layer. It is believed that the etching may alter

Korvikt [17]

Answer:

the ratio of the etched to the original crack tip radius is 30.24

Explanation:

Given the data in the question;

we determine the initial fracture stress using the following expression;

(σf)₁ = 2(σ₀)₁ $[$ α₁/( $p_t$ )₁ $]^{1/2$ ----- let this be equation 1

where; (σ₀)₁ is the initial fracture strength

( $p_t$ )₁ is the original crack tip radius

α₁ is the original crack length.

first, we determine the final crack length;

α₂ = α₁ - 16% of α₁

α₂ = α₁ - ( 0.16 × α₁)

α₂ = α₁ - 0.16α₁

α₂ = 0.84α₁

next, we calculate the final fracture stress;

the fracture strength is increased by a factor of 6;

(σ₀)₂ = 6( σ₀ )₁

Now, expression for the final fracture stress

(σf)₂ = 2(σ₀)₂ $[$ α₂/( $p_t$ )₂ $]^{1/2$ ------- let this be equation 2

where ( $p_t$ )₂ is the etched crack tip radius

value of fracture stress of glass is constant

Now, we substitute 2(σ₀)₁ $[$ α₁/( $p_t$ )₁ $]^{1/2$ from equation for (σf)₂ in equation 2.

0.84α₁ for α₂.

6( σ₀ )₁ for (σ₀)₂.

∴

2(σ₀)₁ $[$ α₁/( $p_t$ )₁ $]^{1/2$ = 2(6( σ₀ )₁) $[$ 0.84α₁/( $p_t$ )₂ $]^{1/2$

divide both sides by 2(σ₀)₁

$[$ α₁/( $p_t$ )₁ $]^{1/2$ = 6 $[$ 0.84α₁/( $p_t$ )₂ $]^{1/2$

$[$ 1/( $p_t$ )₁ $]^{1/2$ = 6 $[$ 0.84/( $p_t$ )₂ $]^{1/2$

$[$ 1/( $p_t$ )₁ $]$ = 36 $[$ 0.84/( $p_t$ )₂ $]$

1 / ( $p_t$ )₁ = 30.24 / ( $p_t$ )₂

( $p_t$ )₂ = 30.24( $p_t$ )₁

( $p_t$ )₂/( $p_t$ )₁ = 30.24

Therefore, the ratio of the etched to the original crack tip radius is 30.24

6 0

3 years ago

Q4. (20 points) For a bronze alloy, the stress at which plastic deformation begins is 271 MPa and the modulus of elasticity is 1

babunello [35]

Answer:

a) P = 86720 N

b) L = 131.2983 mm

Explanation:

σ = 271 MPa = 271*10⁶ Pa

E = 119 GPa = 119*10⁹ Pa

A = 320 mm² = (320 mm²)(1 m² / 10⁶ mm²) = 3.2*10⁻⁴ m²

a) P = ?

We can apply the equation

σ = P / A ⇒ P = σ*A = (271*10⁶ Pa)(3.2*10⁻⁴ m²) = 86720 N

b) L₀ = 131 mm = 0.131 m

We can get ΔL applying the following formula (Hooke's Law):

ΔL = (P*L₀) / (A*E) ⇒ ΔL = (86720 N*0.131 m) / (3.2*10⁻⁴ m²*119*10⁹ Pa)

⇒ ΔL = 2.9832*10⁻⁴ m = 0.2983 mm

Finally we obtain

L = L₀ + ΔL = 131 mm + 0.2983 mm = 131.2983 mm

3 0