Answer the following questions, and very briefly explain your answer:

alexandr1967 [171]

Answer:

A) micro defects are left behind on the surface of metal components during the manufacturing process. These defects, in the form of micro-cracks or pits, becomes initiation sites for crack propagation or corrosion. Removing these imperfections on the surface of metal parts by electroplating greatly improves the life of metal components.

B) it will reduce fatigue crack growth.

Dispersion hardening involves the inclusion of small, hard particles in the metal, thus restricting the movement of dislocations, and thereby raising the strength properties. In dispersion hardening it is assumed that the precipitates do not deform with the matrix and that a moving dislocation bypasses the obstacles (precipitates) by moving in the clean pieces of crystal between the precipitated particles.

C) stress concentrations such as changes in section with sharp corners caused yielding, which will typically occur first at a stress concentration. For ductile materials localised plastic deformation can cause a redistribution of stress, enabling the component to continue to carry load. Brittle materials will typically fail at the stress concentration. Repeated loading may cause a fatigue crack to initiate and slowly grow at a stress concentration leading to the failure of even ductile materials. Fatigue cracks always start at stress raisers, so removing such defects increases the fatigue strength.

5 0

3 years ago

What is kirchoff's current law?

Anastaziya [24]

Answer:

The sum of all currents entering a junction is 0

Explanation:

Current cannot disappear, so the currents leaving a junction have to equal the currents entering a junction. If you would give the currents leaving the junction an opposite sign (e.g., negative) it implies that the sum of all these currents is exactly 0.

4 0

4 years ago

Read 2 more answers

The viscosity of the water was 2.3×10^−5lb⋅⋅s/ft^2 and the water density was 1.94 slugs/ft^3. Estimate the drag on an 88-ft diam

Lina20 [59]

Answer:

hello your question is incomplete attached below is the complete question

answer : Drag force = 1.3 Ib

Explanation:

we have to represent the dimensions of the drag force in terms of FLT

i.e : D = f( <em>d,v,p,u </em>) represented in terms of FLT

D = F , V = LT^-1, d = L, p = FL^-4 T^2

u = FL^-2 T, Number of independent terms = 5

attached below is the detailed solution

6 0

4 years ago

A machine used to shred cardboard boxes for composting has a first cost of $10,000, an AOC of $7000 per year, a 3-year life, and

borishaifa [10]

Annual Payment where F is accumulated sum of amount, n is number of years and i is annual rate of interest. The standard notation equation is in the image since i can’t type it-

6 0

3 years ago

A car is traveling at sea level at 78 mi/h on a 4% upgrade before the driver sees a fallen tree in the roadway 150 feet away. Th

Dmitrij [34]

Answer: V = 47.7 mi/hr

Explanation:

first we calculate elements of aero-dynamic resistance

Ka = p/2 * CD * A.f

p is the density of air(0.002378 slugs/ft^3) for zero altitude, CD is the drag coefficient(0.35) and A.f is the front region of the vehicle

so we substitute

Ka = 0.002378/2 * 0.35 * 18

Ka = 0.00749

Now we calculate the final speed of the vehicle (V2) using the relation;

S = (YbW/2gKa)In[ (UW + KaV1^2 + FriW ± Wsinθg) / (UW + KaV2^2 + FriW ± Wsinθg)

so

WE SUBSTITUTE

150 = (1.04 * 2700 / 2 * 32.2 * 0.0075) In [(0.8 * 2700 + 0.0075 *(78mil/hr * 5280ft/1min * 1hr/3600s)^2 + 0.017 * 2700 ± 2700 * 0.04) / (0.8 * 2700 + 0.0075 * V2^2 + 0.017 * 2700 ± 2700 * 0.04)]

150 = (2808/0.483) In [(2160 + 98.16 + 153.9) / ( 2160 + 0.0075V2^2 + 153.9)]

150 = 5813.66 In [ (2160 + 98.16 + 153.9) / ( 2160 + 0.0075V2^2 + 153.9)]

divide both sides by 5813.66

0.0258 = In [ (2412.06) / ( 0.0075V2^2 + 2313.9)]

take the e^ of both side

e^0.0258 = (2412.06) / ( 0.0075V2^2 + 2313.9)

1.0261 = (2412.06) / ( 0.0075V2^2 + 2313.9)]

(0.0075V2^2 + 2313.9) = 2412.06 / 1.0261

(0.0075V2^2 + 2313.9) = 2350.7

0.0075V2^2 = 2350.7 - 2313.9

0.0075V2^2 = 36.8

V2^2 = 36.8 / 0.0075

V2^2 = 4906.6666

V2 = √4906.6666

V2 = 70.0476 ft/s

converting to miles per hour

V2 = 70.0476 ft/s * 1 mil / 5280 ft * 3600s / 1hr

V = 47.7 mi/hr

8 0

3 years ago

Please help Here is the question